Polipropilen va qatlamli silikatlar asosida nanokompozitlar olish va ularning strukturaviy va mexanik xossalari
Keywords:
polipropilen, closite20a, kompozit, maleinlangan polipropilen, interkalyatsiya, eksfoliatsiya, montmorillonitAbstract
Polipropilen (PP), fizik-mexanik va harorat xususiyatlari tufayli mashinasozlik va elektrotexnika sanoatida keng qo'llaniladi. PP makromolekulalarining degradatsiyasi tufayli termal ta'sir qilish jarayonida elastiklik kuchini yo'qotishi kuzatiladi. Olingan ma'lumotlar polipropilenni qayta ishlash shartlarini tanlash uchun qiziqish uyg'otadi.
References
Korakianiti, Athina, et al. "Characterization of polypropylene (PP) nanocomposites for industrial applications." Macromolecular Symposia. Vol. 205. No. 1. Weinheim: WILEY‐VCH Verlag, 2004.
Zhang, Guizhen, et al. "Preparation of polymer/clay nanocomposites via melt intercalation under continuous elongation flow." Composites Science and Technology 145 (2017): 157-164.
Cao, Jing, Na Wen, and Yuying Zheng. "The preparation of calcium pimelate modified OMMT from natural Ca-montmorillonite and its application as β-nucleating agent for polypropylene." Polymer Testing 65 (2018): 352-359.
Al-Samhan, Meshal, et al. "Comparative effects of MMT clay modified with two different cationic surfactants on the thermal and rheological properties of polypropylene nanocomposites." International Journal of Polymer Science 2017 (2017).
Hasegawa, Naoki, et al. "Preparation and mechanical properties of polypropylene-clay hybrids based on modified polypropylene and organophilic clay." Journal of Applied Polymer Science 78.11 (2000): 1918-1922.
Yuan, Q., and R. D. K. Misra. "Impact fracture behavior of clay-reinforced polypropylene nanocomposites." Polymer 47.12 (2006): 4421-4433.
Zdiri, K., A. Elamri, and M. Hamdaoui. "Advances in thermal and mechanical behaviors of PP/clay nanocomposites." Polymer-plastics technology and engineering 56.8 (2017): 824-840.
Utracki, Leszek A. Clay-containing polymeric nanocomposites. Vol. 1. iSmithers Rapra Publishing, 2004.
Minardi, A., et al. "The effect of the moulding conditions on the semicrystalline structure of polypropylene." Polymer 38.15 (1997): 3957-3965.
Foresta, T., S. Piccarolo, and G. Goldbeck-Wood. "Competition between α and γ phases in isotactic polypropylene: effects of ethylene content and nucleating agents at different cooling rates." Polymer 42.3 (2001): 1167-1176.
Dong, Yu, and Debes Bhattacharyya. "Dual role of maleated polypropylene in processing and material characterisation of polypropylene/clay nanocomposites." Materials Science and Engineering: A 527.6 (2010): 1617-1622.
Duvall, J., et al. "Interfacial effects produced by crystallization of polypropylene with polypropylene‐g‐maleic anhydride compatibilitzers." Journal of applied polymer science 52.2 (1994): 207-216.
Эшбекова, С. О., Ибрагимов, Ж. К., Ашуров, Н. Р., & Хакбердиев, Э. О. (2020). НАНОКОМПОЗИТЫ НА ОСНОВЕ ПОЛИПРОПИЛЕНА. «Узбекский физический журнал», 22(6), 369-373.
Eshbekova, S. O., Ibragimov, J. K., & Yaxshilikov, K. U. (2022). Nanokompozitlar olish va ularning strukturaviy va mexanik xossalari. Science and Education, 3(11), 558-562.
Эшбекова, С. О., & Ибрагимов, Ж. К. ПОЛИПРОПИЛЕН НАНОКОМПОЗИТЛАРИНИНГ МЕХАНИК ХАРАКТЕРИСТИКАЛАРИ. Узбекско-Казахский Симпозиум «Современные проблемы науки о полимерах» СБОРНИК ТЕЗИСОВ, 158.
Эшбекова, С. О., Ибрагимов, Ж. К., Ашуров, Н. Р., & Хакбердиев, Э. О. (2023). НАНОКОМПОЗИТЫ НА ОСНОВЕ ИЗОТАКТИЧЕСКОГО ПОЛИПРОПИЛЕНА. ОБРАЗОВАНИЕ НАУКА И ИННОВАЦИОННЫЕ ИДЕИ В МИРЕ, 22(2), 89-96.
Ибрагимов, Ж. К., & Яхшиликов, К. У. (2022). ПОЛИПРОПИЛЕН НАНОКОМПОЗИТЛАРИНИНГ СТРУКТУР-ХОССАЛАРИНИНГ КОРРЕЛЯЦИОН БОҒЛИҚЛИГИ. Экономика и социум, (9 (100)), 352-356.
Ибрагимов, Ж. К., & Яхшиликов, К. У. (2022). НАНОКОМПОЗИТНЫЕ ПОЛИМЕРНЫЕ МАТЕРИАЛЫ НА ОСНОВЕ ОРГАНОГЛИН. Экономика и социум, (9 (100)), 347-351.
Berdinazarov, Q. N., Khakberdiev, E. O., Normurodov, N. F., & Ashurov, N. R. (2022). Mechanical and Thermal Degradation Properties of Isotactic Polypropylene Composites with Cloisite15A and Cloisite20A.
Berdinazarov, Q., Normurodov, N., Khakberdiev, E., Sadykov, S., Ashurov, N., & Riskulov, A. (2020). ЗАВИСИМОСТЬ УПРУГО-ПРОЧНОСТНЫХ ХАРАКТЕРИСТИК ИЗОТАКТИЧЕСКОГО ПОЛИПРОПИЛЕНА J-170T И БЛОК-СОПОЛИМЕРА ПРОПИЛЕНА С ЭТИЛЕНОМ JM-370 ОТ ТЕМПЕРАТУРЫ И ЧИСЛА ЭКСТРУЗИИ. SCIENCE AND INNOVATIVE DEVELOPMENT, 3(4), 176-184.